Color Stability, Surface Roughness and Flexural Strength of an Acrylic Resin Submitted to Simulated Overnight Immersion in Denture Cleansers

This study evaluated color stability, surface roughness and flexural strength of acrylic resin specimens after immersion in alkaline peroxide and alkaline hypochlorite, simulating a period of one and a half year of use of overnight immersion. Sixty disc-shaped (16X4 mm) and 80 rectangular specimens (65X10X3.3 mm) were prepared from heat-polymerized acrylic resin (Lucitone 550) and distributed into 4 groups (n=20): C1: without immersion, C2: 8 h immersion in distilled water; AP: 8 h immersion in alkaline peroxide effervescent tablet; SH: 8 h immersion in 0.5% NaOCl solution. Properties were evaluated at baseline and after the immersion. Color data were also calculated according the National Bureau of Standards (NBS). Results were analyzed statistically by ANOVA and Tukey's HSD test (α=0.05). AP (2.34 ± 0.41) caused color alteration significantly higher than C2 (0.39 ± 0.30) and SH (1.73 ± 0.52). The mean ΔE values were classified as indicial for C2 (0.36 ± 0.29) and noticeable for AP (2.12 ± 0.39) and SH (1.59 ± 0.48). SH (0.0195 ± 0.0150) caused significantly higher ΔRa (p=0.000) than the C2 (0.0005 ± 0.0115) and PA (0.0005 ± 0.0157) groups. There was no statistically significant difference (p=0.063) among the solutions for flexural strength (C1: 105.43 ± 14.93, C2: 100.30 ± 12.43, PA: 97.61 ± 11.09, SH: 95.23 ± 10.18). In conclusion, overnight immersion in denture cleansing solutions simulating a year and a half of use did not alter the flexural strength of acrylic resin but caused noticeable color alterations, higher for alkaline peroxide. The 0.5% NaOCl solution caused increase in surface roughness.

Resumo O estudo avaliou a alteração de cor, rugosidade de superfície e força de flexão de espécimes de resina acrílica após imersão em peróxido alcalino e hipoclorito alcalino, simulando um ano e meio de uso seguindo a imersão noturna. Sessenta espécimes circulares (16 X 4 mm) e oitenta retangulares (65 X 10 X 3,3 mm) de resina acrílica termopolimerizável (Lucitone 550) foram distribuídos em 4 grupos (n=20): C1: sem imersão, C2: 8 h de imersão em água destilada; PA: 8 h de imersão em pastilhas efervescentes de peróxido alcalino; HS: 8 h de imersão em hipoclorito de sódio a 0,5%. As propriedades foram avaliadas antes e após as imersões. Os dados de alteração de cor também foram calculados de acordo com o National Bureau of Standards (NBS). Os dados foram analisados estatisticamente pelo teste ANOVA e Tukey HSD (α=0,05). O PA (2,34 ± 0,41) causou alteração de cor significativamente maior que C2 (0,39 ± 0,30) e SH (1,73 ± 0,2). A média ΔE foi classificada como indicial para C2 (0,36 ± 0,29) e perceptível para PA (2,12 ± 0,39) e HS (1,59 ± 0,48). HS (0,0195 ± 0,0150) causou significantemente maior ΔRa (p=0) do que os demais (C2: 0,0005 ± 0,0115 e PA: 0,0005 ± 0,0157). Não houve diferença estatisticamente significante (p=0,063) entre as soluções para a resistência à flexão (C1: 105,43 ± 14,93; C2: 100,30 ± 12,43, PA: 97,61 ± 11,09, HS: 95,23 ± 10,18). A imersão noturna em soluções higienizadores de próteses simulando um ano e meio de uso não alterou a resistência à flexão da resina acrílica, porém causou alterações perceptíveis de cor, sendo maiores com o peróxido alcalino. O hipoclorito de sódio a 0,5% ...

Alkaloid-rich fraction of Himatanthus lancifolius contains anti-tumor agents against leukemic cells

The effects of the alkaloid-rich fraction of Himatanthus lancifolius (Müll. Arg) Woodson on normal marrow cells and leukemic cell lines were investigated. After 48 h exposure, the proliferation assay showed significant cell growth inhibition for Daudi (0.1-10 µg/mL), K-562 (1-10 µg/mL), and REH cells (10-100 µg/mL), yet was inert for normal marrow cells. A similar inhibition profile was observed in clonogenic assays. This alkaloid-rich fraction, in which uleine is the main compound, showed no signs of toxicity to any cells up to 10 µg/mL. Cell feature analyses after induction of differentiation showed maintenance of the initial phenotype. Flow cytometric expression of Annexin-V and 7-AAD in K-562 and Daudi cells has indicated that the cells were not undergoing apoptosis or necrosis, suggesting cytostatic activity for tumor cells.

Os efeitos da fração rica em alcalóides indólicos de Himatanthus lancifolius (Müll. Arg) Woodson sobre células normais de medula óssea e linhagens celulares leucêmicas foram investigados. Após 48 horas de exposição, os ensaios de proliferação demonstraram efeitos inibitórios significativos para as linhagens Daudi (0,1-10 µg/mL), K-562 (1-10 µg/mL) e REH (10-100 µg/mL), enquanto mostrou-se inerte sobre células normais de medula óssea. Os perfis de inibição se repetiram nos ensaios clonogênicos. A fração rica em alcalóides, na qual a uleína é a substância majoritária, não demonstrou toxicidade até a dose de 10 µg/mL para nenhuma das células incluídas no estudo. Da mesma forma, não se observou influência dessa fração sobre a diferenciação celular dessas linhagens, mas manutenção de seu estado maturacional inicial. O conjunto de dados descritos associado à baixa co-expressão de anexina-V e 7-AAD sugerem que esta fração exerce atividade citostática para células tumorais.